Flyboat lightning-chip varistor (MOV) low-cost irrigation glue Description

Column:Company News Time:2019-12-04 Browsing volume: 3493
shared:

  To solve the pressure-sensitive mine-chip low-cost epoxy resin casting, I specifically purchased the company in Tianjin Jinqiao Insulation Materials Co., Ltd. tens of kilograms TXH-1156 epoxy potting material, will be my company in 2006 in the first half of approved sub-products remaining extract a few pieces of each sample to 10 the number of films of epoxy potting test results the following table: (left sample has been due to the long putting-damp, encapsulation is not carried out before the drying processing)

Chip LotPotting ago ParametersCasting process 5 days curing parameters 15 days curing parameters Notes
U 1mAI L (μA)U 1mAI L (μA)U 1mAI L (μA)
 0601-1 615V8.3

 120ml gel +30 ml curing agent (volume ratio 4:1, weight ratio 100:10), and mix thoroughly 8min, room temperature curing.

 616V7.36176.2
608V11.4611V9.56109.1
632V6.4626V5.86255.0
 637V7.4638V6.56396.0
 0603-3 702V10.5703V9.37058.4
705V18.1712V14.070912.6
716V18.7722V17.672015.5
705V13.3708V8.47077.8
 725V16.9729V15.172813.6
 0604-1705V12.4 704V 10.17069.4
 693V8.6692V6.46956.5
716V18.7713V15.271613.3
 0604-5673V7.5 673V6.7 6.7674 6746.3
676V13.5 677V11.3677 10.8 
 669V7.2 670V6.16715.8
 660V10.6661V8.86648.8
666V9.7667V7.16676.7 
0605-A2664V6.2

 200ml gel +40 ml curing agent (volume ratio 5:1, weight ratio of 100:8), and mix thoroughly 10min, room temperature curing.

656V4.56593.6
670V16.5667V5.76685.4 
657V13.0653V5.16475.1
663V8.0660V5.16595.0.
663V8.6663V5.86545.8
652V8.8652V5.66635.4
666V5.1 660V5.06535.0

  The results can be seen from the above: As long as the proportion of appropriate technology is correct, can be used to reduce the user-made epoxy resin casting cost (the other properties of rubber user-authentication). My company filling plastic processes are as follows:

  Before the first chip encapsulation under 120 ℃ drying 30 to 60 minutes; rubber, curing agent in accordance with 5:1 volume ratio (100g: 8g = 8ml weight ratio) with a good mix thoroughly, and mix thoroughly how to adjust the amount of time under the gum, but it should be ensure the full mix well; and then proceed to filling glue. Kaifeng, a longer time if the glue should be heated to glue 80 ~ 100 ℃, thermal insulation of about 30min in order to drive out moisture, cooling and curing agent and then allocated in proportion to the use of a good mix thoroughly.  Potting after basic curing the product placed in the oven for 85 ~ 100 ℃ heat insulation 30 ~ 60 minutes.

  Use of other adhesive is also important to note that the user reduce the ratio of curing agent is generally from the manufacturers recommended ratio of 1 / 2 or so begin to try and curing agent dosage should not exceed manufacturer’s recommended maximum ratio of 2 / 3.